"Dear Mr.Jaidev
silver nanoparticles does not follow any particular pathway or signalling mechanism to get enter the cell.
Silver nanoparticles entrance in cell can be compared with killing somebody with bullet. One possible mechanism could be phago…"
silver nanoparticles does not follow any particular pathway or signalling mechanism to get enter the cell.
Silver nanoparticles entrance in cell can be compared with killing somebody with bullet. One possible mechanism could be phago…"
"Dear Asim
For your prepared Cu nanoparticles in DI water, my suggestion is that you first get sure that they are in the mettalic form. As Cu nanoparticles are very much prone to oxidation giving copper oxide.
Second, you can go for lyophilization, t…"
For your prepared Cu nanoparticles in DI water, my suggestion is that you first get sure that they are in the mettalic form. As Cu nanoparticles are very much prone to oxidation giving copper oxide.
Second, you can go for lyophilization, t…"
"What about bringing out a nanopaprika song?"
"Hi the problem is not with the solvent.
1. disperse your samples in ethanol
2. Sonicate for few seconds
3. let big particles settle down for few seconds
4. Hold the grid using a twizer in air
5. pick a drop from the upper portion of the solvent usin…"
1. disperse your samples in ethanol
2. Sonicate for few seconds
3. let big particles settle down for few seconds
4. Hold the grid using a twizer in air
5. pick a drop from the upper portion of the solvent usin…"
"it may be the process you adopted for the synthesis giving you the morphology what you probably seeing in TEM. Did you did SEM?
If you have doubt using ethanol use DI water then but it will take a bit long to dry so place the grid between two glass…"
If you have doubt using ethanol use DI water then but it will take a bit long to dry so place the grid between two glass…"
"Please contact Prof. Ashutosh, Head, Nanoscience Centre, IIT-Kanpur. He has got good facility for AFM."
"Hi Wolf,
I was not repulsive to your remark. I am rather apologetic if my writing has pain you. Yes you are factual that this forum is not about philosophy. However, Science over all is a philosophy in itself.
I already appreciated your idea of the…"
I was not repulsive to your remark. I am rather apologetic if my writing has pain you. Yes you are factual that this forum is not about philosophy. However, Science over all is a philosophy in itself.
I already appreciated your idea of the…"
"The word “complaining” is the usual rubbish that the mind loves to chew on. So Wolf, my writing this blog is not at all about complaining. If this would have been the case, you wouldn’t have posted the reply. Isn’t it?
Your reply can be seen from t…"
Your reply can be seen from t…"
"Hi Jafar
Thanks for friend invitation.
It will be all my pleasure to discuss with you on silver nanoparticles.
regards
vyom"
Thanks for friend invitation.
It will be all my pleasure to discuss with you on silver nanoparticles.
regards
vyom"
"Hi shivam
you can catch me @
vyomparashar@gmail.com"
you can catch me @
vyomparashar@gmail.com"
"Hi Fisher
You can prepare Silver nanoparticles (Ag NPs) by two routes physical and chemical.
of which physical route will be bit costly, the best physical route in terms of cost efficiency could be laser ablation.
Otherwise, chemical routes and bi…"
You can prepare Silver nanoparticles (Ag NPs) by two routes physical and chemical.
of which physical route will be bit costly, the best physical route in terms of cost efficiency could be laser ablation.
Otherwise, chemical routes and bi…"
"Thanks Prof. for you encourgement"
"Hi priyanka
new year wishes!
Does Bioxcel has some future plans in bionanotechnology?
regards
vyom"
new year wishes!
Does Bioxcel has some future plans in bionanotechnology?
regards
vyom"
"Thank you Prof. for liking the design, we can discuss further to expand the concept of design"
Comments
i think now we are in knowledge society,more visions ,more virtualism
your diagram design for nanouniversity and nanocity present idea for the relation between nanouniversity and nanocity and the nanouniversity as the centre of important elements of nanocity
the project acceptable for discussion
Thats true but i will appreciate your vision in this. Hope you will spare some of your time and explain us all a bit more about the vision. This will help us all to give and disscuss our inputs.
and yes thanks for being a friend.
thanks for your comment to nanouniversity,
yse the graphics need mutch explanations,also need more discussions
andras paszternak, editor