"Zero dim is nothing but quantum dot. The size will be approximately <10nm. Comparable to its bohr atomic radius the particle size will vary. So u cant tell that all particles less than 10 nm are quantum dots.It will vary from material to material. I…"
"Thank u so much.."
"Centrifuge and you can easily separate particles. Decant the solution and then dry the particles in a hot air oven."
"Thank you Sundararajan.T."
"Ya.. If you are interested let us proceed.."
"Actually Im talking about Solid Oxide Fuel cell so there is no problem of leakage. It is a solid material with anode, cathode and solid oxide electrolyte. The material must be kept in a tubular furnace and heated I suppose. So a special arrangement…"
"I need electrochemical impedence ie, arrhenius plots and complex impedance plots for materials prepared for application in fuel cell at temperature from 400 to 800 degree C. It would be also good if i get I-V and I-P characteristics."
"U can try clear dispersion of the nanocrystallite sample in hexane and put drops of it on a carbon-coated copper grid to get TEM image."
"U can write GATE Exam and do ur Ph.D in IITs. U may also apply to various universities of your interest. But the main thing is you have to get a good guide and place where u have good lab facilities."
I am working on ionic conducting nanocomposites at intermediate temperature. I am in immense need of help for carrying out impedance analysis for my samples in both pellet form and thin film at temperatures upto 800 C. Moreover I assure you to give…