A large number of oxide-containing group surface, having a good solvent solubility and the affinity of the polymer.
Oxygen content of oxygen-containing groups is 30 to 40%, very good water-soluble, single content is more than 99% after the dissolution. Microchip size 0.5 ~ 3μm, the thickness is about 0.55 ~ 1.2nm. No precipitation.
Graphene oxide powder is obtained by drying graphene oxide sol by vacuum freeze. Graphene oxide in a freeze-drying process is not lost due to the drying surface temperature oxygen-containing groups and caused between graphene oxide layers overlap. After drying the powder porous, spongy, water was added, Sonicator ultrasonic 5-10min (ultrasonic cleaning, ultrasonic about 30min), the sol can be restored to the original characters to obtain a uniform and stable dispersion.
Purity:> 99wt%
Thickness: 0.55 ~ 1.2nm
Diameter: 0.5 ~ 3μm
Layers: 1-10 layer
Color: Amber

Main types following:
Graphene oxide powder
Description:
brown to yellow color powder
Average Purity>99%
Specific Surface Area~65 m2/g
C/O Atomic Ratio 0.8-1.6 adjustable
1 Layer Thickness 0.6-0.8nm
Lateral Dimension 200nm~10μm

High-activity Graphene oxide powder
Description:
Preparation: improved Hummers
brown to yellow color powder
Average Purity>99%
Specific Surface Area~65 m2/g
C/O Atomic Ratio 0.8-1.5 adjustable
1 Layer Thickness 0.6-0.8 nm
Lateral Dimension 200nm~10μm

Graphene oxide solution
This product was prepared by improved Hummers, and then sonicated in water to obtain a stable graphene oxide solution.Concentration range is 0.1-3mg/mL. For scientific research use.

Description:
Homogenized golden yellow or brown liquid
pH 5-7
Concentration 0.1-3mg/mL
C/O Atomic Ratio 0.8-1.5 adjustable
1 layer Rate>95%
1 Layer Thickness 0.7-1.2nm
Lateral Dimension 200nm-10μm

Graphene oxide hydrosol
The product is purified after repeated washing and stripping of undiluted graphite oxide puree. Without drying throughout the production process, so the rich oxygen-containing functional groups are effectively retained, can be prepared graphene oxide solution by mild aqueous ultrasound. This product is a laboratory preparation for scientific research use.

Description:
Homogenized brown Collosol liquid
pH 5-7
Concentration 7-10mg/mL
C/O Atomic Ratio 0.8-1.5 adjustable
1 layer Rate >50%
1 Layer Thickness 0.7-1.2nm
Lateral Dimension 200nm-10μm

www.nanochemi.com